At present, innovacera’s alumina ceramics material is including two types: high-purity and ordinary.
The high-purity alumina ceramic series is the ceramic material with Al2O3 content of over 99.9%. Due to its sintering temperature up to 1650-1990C and transmission wavelength of 1 ~ 6μm, it is usually made into molten glass to replace the platinum crucible: Cause its light transmittance and alkali metal corrosion resistance, it can be used as a sodium tube for HID application; in the electronics industry, it can be used as integrated circuit ceramics substrate and high-frequency insulating materials.
According to the difference in Al2O3 content, the ordinary type alumina ceramic series is divided into 99 ceramics, 95 ceramics, 90 ceramics, 85 ceramics etc. The ceramics with Al2O3 content of 80% or 75% is also classified as ordinary alumina ceramic series. Innovacera produce alumina all is above 92% Alumina.
Among these, 99 alumina ceramic materials are used for producing high-temperature crucible, refractory furnace tubes and special wear-resistant materials such as ceramic bearings, ceramic seals and valve films and so on.
95 alumina ceramics are mainly used as corrosion-resistant and wear-resistant parts.
85 ceramics are often mixed in some steatites, thus improving electrical performance and mechanical strength.
It can be sealed with molybdenum, niobium, tantalum and other metals and some are used as electro-vacuum devices.